亚共晶Al-Si合金初生相的EBSD表征
邓 超*,刘如学,洪 睿,郑 江
(重庆大学材料科学与工程学院,重庆 400043)
摘 要 利用电子背散射衍射(EBSD)技术对亚共晶Al-Si合金进行了表征。根据晶界成像图与花样质量成像图提取了初生α-Al相的取向数据,通过合理设置晶界临界值与带衬度值均可获得可靠的结构参数统计结果,提取出的初生α-Al相信息可以方便地分析其含量、形态、尺寸、分布以及取向等信息。
关键词 Al-Si合金;电子背散射衍射技术(EBSD);初生相
中图分类号:TG115.21+5.3 文献标识码:A doi:10.3969/j.issn.1000-6281.2017.01.003
EBSD characterization of primary phase in a hypoeutectic Al-Si alloy
DENG Chao, LIU Ru-xue, HONG Rui, ZHENG Jiang
(College of Materials Science and Engineering, Chongqing University, Chongqing 400043)
Abstract Electron backscatter diffraction technique (EBSD) was used to characterize a hypoeutectic Al-Si Alloy. The orientation data of primary α-Al phase was extracted by grain boundary map and pattern quality map. The reliable statistic results on microstructure parameters can be obtained by setting reasonable grain boundary value and band contrast value. The detailed information of content, morphology, size, distribution, and orientation, etc. can be well analyzed by the obtained results of primary α-Al phase.
Keywords Al-Si alloy; electron backscatter diffraction technique (EBSD); primary phase
全文下载请到中国知网,万方数据或重庆维普等数据库中下载!
[1] DAHLE A K,NOGITA K,ZINDEL J W,et al. Eutectic nucleation and growth in hypoeutectic Al-Si alloys at different strontium levels[J]. Metall Mater Trans A,2001,32: 949–960.
[2] CHEN Z W,HAO X L,ZHAO J,et al. Kinetic nucleation of primary α(Al) dendrites in Al-7%Si-Mg cast alloys with Ce and Sr additions[J]. Trans Nonferrous Met Soc China (English ed.),2013,23: 3561–3567.
[3] HWANG J Y,DOTY H W,KAUFMAN M J. The effects of Mn additions on the microstructure and mechanical properties of Al-Si-Cu casting alloys[J]. Mater Sci Eng A,2008,488: 496–504.
[4] 杨明波,潘复生,彭晓东,等. 压力铸造对亚共晶Al-11Si-1.8Cu合金的组织细化作用[J]. 重庆大学学报(自然科学版),2005,28: 9-12.
[5] 陈绍兰,闫洪,唐永春. 铸造亚共晶Al-Si合金显微组织中α枝晶相的定量分析[J]. 铸造技术,2010,31: 1215–1217.
[6] ZHANG J,YU H,KANG S B,et al. Electron backscattered diffraction analysis of eutectic solidification in a continuous cast aluminum alloy billet[J]. Mater Manuf Process,2014,29: 472–476.
[7] NOGITA K,DAHLE A K, Eutectic solidification in hypoeutectic Al-Si alloys: electron backscatter diffraction analysis[J]. Mater Charact,2001,46: 305–310.
[8] LI X,FAUTRELLE Y,GAGNOUD A,et al. EBSD study of the influence of a high magnetic field on the microstructure and orientation of the Al-Si eutectic during directional solidification[J]. Metall Mater Trans A,2016,47: 2952–2963.
[9] 刘庆, 电子背散射衍射技术及其在材料科学中的应用[J]. 中国体视学与图像分析,2005,10: 205–210.
[10] LIU X,ZHANG Y,BEAUSIR B,et al. Twin-controlled growth of eutectic Si in unmodified and Sr-modified Al-12.7%Si alloys investigated by SEM/EBSD[J]. Acta Mater,2015,97: 338–347.
[11] WRIGHT S I,NOWELL M M. EBSD image quality mapping[J]. Microsc Microanal,2006,12: 72–84.