镍基单晶高温合金孔洞区域蠕变行为原位SEM研究
何文玲,吕俊霞,程晓鹏,王 晋,张跃飞* ,张 泽
(1.北京工业大学 材料与制造学部,北京100124;2.浙江大学 材料科学与工程学院,浙江 杭州310027)
摘 要 本文采用扫描电镜(SEM)原位高温蠕变实验研究方法,在780 ℃/720 MPa的蠕变条件下,对镍基单晶高温合金开展蠕变实验,实时观察了孔洞区域显微组织原位演化过程。实验结果表明:蠕变开始后孔洞处应力集中,变形集中于孔洞区域,孔洞旁产生45°及135°方向以及垂直于应力轴的裂纹,多个孔洞共同作用可引起颈缩。颈缩发生后真实应力增加,促进颈缩区孔洞处裂纹垂直于应力轴扩展,而非颈缩区裂纹在切应力作用下沿45°以及135°方向发生扩展。此外蠕变第一阶段已经发生颈缩,导致第二以及第三阶段时间较短,缩短蠕变寿命。揭示了高温下孔洞缺陷对蠕变行为的影响规律及机制,对蠕变寿命预测及高温合金研发有一定启发意义。
关键词 镍基单晶高温合金;原位蠕变;颈缩;孔洞;裂纹
中图分类号:TG132. 3;TG146. 1+ 5;TG115. 21+ 5. 3 文献标识码:A doi:10.3969/j.issn.1000-6281.2022.05.005
In-situSEM study on creep behavior in hole region of nickel-based single crystal superalloy
HE Wen-ling1, LU Jun-xia1, CHENG Xiao-peng1, WANG Jin2, ZHANG Yue-fei2*, ZHANG Ze2
(1.Faculty of Materials and Manufacturing,Beijing University of Technology,Beijing 100124;
2. School of materials science and engineering, Zhejiang University, Hangzhou Zhejiang 310027,China)
Abstract Scanning electron microscopy (SEM) was used to investigate the in-situ creep behavior of nickel-based single crystal superalloy at 780 ℃/720 MPa. Microstructural evolution in hole areas was observed in real time. The experimental results show that the stress concentration leads to the deformation concentrated in the hole areas, and the cracks along 45°and 135°directions and perpendicular to the stress axis are generated. The joint action of multiple holes leads to the necking. After the necking, the real stress in the necking zone increases, which promotes the crack propagation perpendicular to the stress axis, while the crack propagation along the direction of 45°and 135°in the non-necking zone under the shear stress. In addition, necking has emerged inthe first stage of creep, resulting in the shorter time in the second and third stages of the creep life. This work reveals the effect of hole defectson creep behavior at high temperature, which is instructive for the prediction of creep life and the development of superalloy.
Keywords in situhigh temperature creep;nickel-based single crystal superalloy;hole;necking;crack
“全文下载请到同方知网,万方数据库或重庆维普等数据库中下载!”
[1] 张健, 王莉, 王栋, 等. 镍基单晶高温合金的研发进展[J]. 金属学报,2019, 55 (9): 1078-1094.
[2] POLLOCK T M,TIN S,et al. Nickel-based superalloys for advanced turbine engines: chemistry, microstructure and properties [J]. Journal of Propulsion & Power, 2006, 22: 361-374.
[3] XIA W, ZHAO X, YUE L, et al. Microstructural evolution and creep mechanisms in Ni-based single crystal superalloys:a review [J]. Journal of Alloys and Compounds, 2020, 819: 1-17.
[4] RAE C M F, MATAN N, REED R C. The role of stacking fault shear in the primary creep of [001]-oriented single crystal superalloys at 750 ℃ and 750 MPa [J]. Materials Science and Engineering A, 2001, 300: 125-134.
[5] YU J, LI J, ZHAO J, et al. Orientation dependence of creep properties and deformation mechanism in DD6 single crystal superalloy at 760 ℃ and 785 MPa [J]. Materials Science and Engineering A, 2013, 560: 47-53.
[6] ORLOV M R. Pore formation in single-crystal turbine rotor blades during directional solidification [J]. Russian Metallurgy (Metally), 2008, 2008(1): 56-60.
[7] BOKSTEIN B S, EPISHIN A I, LINK T, et al. Model for the porosity growth in single-crystal nickel-base superalloys during homogenization [J]. Scripta Materialia, 2007, 57: 801-804.
[8] BUCK H, WOLLGRAMM P, PARSA A B, et al. A quantitative metallographic assessment of the evolution of porosity during processing and creep in single crystal Ni-base superalloys [J]. Materialwissenschaft und Werkstofftechni, 2015, 46: 577-590.
[9] GRAVEREND L J, ADRIEN J, CORMIER J. Ex-situ X-ray tomography characterization of porosity during high-temperature creep in a Ni-based single-crystal superalloy: toward understanding what damage is [J]. Materials Science and Engineering A, 2017, 695: 367-378.
[10] ZHANG C, HU W, et al. Creep residual life prediction of a nickel-based single crystal superalloy based on microstructure evolution [J]. Materials Science & Engineering A, 2019, 756: 108-118.
[11] TIAN S, JIANG C, ZHANG S, et al. Influence and analysis of defects on creep behaviors of a single crystal nickel-based superalloy [J]. Materials Science and Engineering A, 2014, 613: 184-192.
[12] 高文杰,桑利军,王晋,等. 基于扫描电镜原位拉伸EBSD-DIC 微观变形研究方法[J]. 电子显微学报,2021, 40(5): 589-594.
[13] 周建力,任潇一,张宜旭,等. 基于扫描电镜原位高温疲劳测试方法研究[J]. 电子显微学报,2021, 40(3): 215-220.
[14] ULLAAH R, LU J, SANG L, et al. In-situ tensile deformation behavior of as-built laser direct metal deposited Ti-6Al-4V alloy at 200 ℃ [J]. Journal of Alloys and Compounds, 2020, 817: 152781.
[15] 赵京浩, 何文玲, 唐亮,等. 一种二代镍基单晶合金750 ℃原位蠕变行为研究 [J]. 电子显微学报,2021, 40(4): 361-366.
[16] 喻健,李嘉荣,史振学, 等. DD6单晶高温合金760℃和1070℃拉伸行为与变形机制[J]. 航空材料学报, 2015, 35(5): 13-20.
[17] 郭建亭. 高温合金材料学:高温合金材料与工程应用[M]. 北京: 科学出版社, 2008.
[18] LI Y, WANG L, ZHAN G, et al. Creep anisotropy of a 3rd generation nickel-base single crystal superalloy at 850 ℃ [J]. Materials Science & Engineering A, 2019, 760: 26-36.
[19] Rae C M F, REED R C. Primary creep in single crystal superalloys: origins, mechanisms and effects [J]. Acta Materialia, 2007, 55:1067-1081.